General Purpose, Patch Fixed, Heat Shrinkable Wraparound Sleeve

• Customization: Available
• Certification: RoHS, ISO
• Color: Black
• Model NO.: WAS-P
• Usage: Electric Wire, Cable Repair & Protection
• Material: Crosslinked Polyolefin
• Type: Heat Shrinkable
• Adhesive Pre-Coat: Yes
• Length(mm): 200,500,750,1000,1500
• Transport Package: Carton Box
• Trademark: United Electric
• Origin: P. R. China
• HS Code: 85472000
• Production Capacity: 1000000PCS/Year

Product Description

WAS-P-General purpose, patch fixed, heatshrinkable wraparound

 

WAS-P is a general purpose, without rail, patch fixed type wraparound sleeve coated with hot melt adhesive.
These wraparound sleeve rely on contact adhesive to hold the sleeve together, ideal for applications where a
stainless steel jointing rail can not be used for either electrical or cosmetic reasons.

 Features

• Offer an easy to apply effective solution for therepair of damaged outer sheaths for all cable types.
• Convenience and easy for installation.
• Suitable for a wide range of cable size.
• Suitable temperature range from -40 ºC to +120 ºC. 
• Material System : Crosslinked Polyolefin
• Power Cable Wrap Technology: Heat Shrink
• Adhesive Coating: Yes
• Mechanical Reinforcement: General purpose
• Power Cable Wrap Shrink Ratio: >3:1
• Component Design: Heat Shrink
• Coating Style: Inline
• Application Diameter (Max): 240mm


Specification
 

Dimensions:
D: Diameter
Da: Diameter as supplied
Db: Diameter after recovery
T: Wall thickness as supplied
L: Length as supplied

   

Type	Application diameter (mm)	D (mm)		T (mm)	L (mm)
		Da min.	Db max.
WAS~P 30/6	8~21	30	8	1.1	410, 910
WAS~P 46/14	18~32	46	14	1.1	410, 910
WAS~P 68/24	31~48	68	24	1.1	410, 910
WAS~P 91/33	43~64	91	33	1.1	410, 910
WAS~P 126/47	61~88	126	47	1.1	410, 910
WAS~P 171/67	88~113	171	67	1.1	410, 910

Technical data

Item	Test method	Typical data
Cross linked polyolefin.
Tensile strength	ASTM D 2671	≥12MPa
Elogation at break	ASTM D 2671	≥300%
Tensile strength after aging (150°C, 168hrs)	ASTM D 2671	≥10MPa
Elogation at break after aging (150°C, 168hrs)	ASTM D 2671	≥200%
Volume resistance	ASTM D 2671	≥1012Ω·cm
Dielectric strength	IEC 60243	≥ 12kV/mm
Water Absorption	ISO62	≤1%
Hot melt adhesive
Softening point	ASTM E28	≥85°C
Water Absorption	ISO62	≤1%