| Type | As supplied | After unrestricted recovery | |||||
| H min | J min | H max | Hw | J max | Jw | P | |
| UE-MPL1 | 24 | 24 | 10 | 2.0 ± 0.1 | 5 | 1.9 ± 0.1 | 28 |
| UE-MPL2 | 30 | 30 | 13.5 | 2.0 ± 0.1 | 6.5 | 1.75 ± 0.1 | 42 |
| UE-MPL3 | 32 | 32 | 17 | 3.0 ± 0.1 | 6.9 | 2.0 ± 0.1 | 40 |
| UE-MPL4 | 36 | 36 | 20 | 3.5 ± 0.1 | 8 | 2.0 ± 0.1 | 60 |
| UE-MPL5 | 43 | 43 | 26 | 4.25 ± 0.1 | 12 | 3.0 ± 0.1 | 60 |
| UE-MPL6 | 53 | 53 | 34 | 4.65 ± 0.1 | 14.5 | 3.5 ± 0.1 | 80 |
| UE-MPL7 | 67 | 67 | 42.4 | 5.8 ± 0.1 | 19 | 3.8 ± 0.1 | 98 |
| Property | Test method | Test result |
| Water absorption | GB 1034-2008 | ≤0.15% |
| Radial change(130±2ºC / 1 ~3min) | ≥50% | |
| Longitudinal change(130±2ºC / 1 ~3min) | ≤10% | |
| Shore hardness(Shore A) | GB 2411-2008 | ≤70 |
| Tensile strength(MPa) | GB/T 1040-2006 | ≥14MPa |
| Ultimate elongation | GB/T 1040-2006 | ≥500% |
| Cold bend(-10±2ºC / 1hr) | UL224-2006 | No cracking |
| Heat shock(136±1ºC / 1hr) | UL224-2006 | No cracking |
| Tensile strength(MPa) | GB/T 1040-2006 | ≥14MPa |
| Ultimate elongation | GB/T 7141-2008 | ≥70% |
| Dielectric strength | GB 1408-2006 | ≥20kV/mm |
| Volume resistivity | GB 1410-2006 | ≥1.0*1013Ω.cm |
| Dielectric constant | GB 1409-2006 | ≤3.5 |
| Flamability(OI) | GB/T 2406-2008 | ≥27.0 |